01902nam a2200325Ia 4500 MX-MdCICY 20260521091752.0 CICY B-21065 The effect of graphene network formation on the electrical, mechanical, and multifunctional properties of graphene/epoxy nanocomposites Composites Science and Technology, 169, p.224-231, 2019 The network formation of reduced graphene oxide (rGO)within an epoxy resin during curing has been in-situ visualised for the first time, with its effect on electrical, mechanical, and multifunctional properties of these nanocomposites explored. Different initial states of dispersion and filler contents were employed to examine the nanofiller network formation process. Good electrical conductivity (10?3?S/m at 0.05?wt percent rGO)together with good mechanical reinforcement (12 percent increase in flexural modulus at 0.2?wt percent rGO)were obtained at relatively low filler loadings. The integrated strain sensing capabilities based on the rGO network were explored with good sensitivity and repeatability. Joule heating was performed as a potential application for de-icing of multifunctional composite components with good heating capability from ?20?°C to 20?°C within 2?min. GRAPHENE EPOXY PERCOLATION ELECTRICAL CONDUCTIVITY MECHANICAL PROPERTIES SENSING DE-ICING Kernin, A. Wan, K. Liu, Y. Shi, X. Kong, J. Bilotti, E. Zhang, H. https://drive.google.com/open?id=1bYw7LC9d3A4R5lcsAR-rL4c2fmHtjZ6d&usp=drive_copy Para ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx Loc REF1 250602s9999 xx |||||s2 |||| ||und|d 31082 31082 0 0 Loc 0 0 F1 CICY CICY RE 2025-06-25 0 B-21065 2025-06-25 16:25:00 2025-06-25 REF1